Sunt decem communiter usus extinguat modi in calor curatio processus, inter se medium (aquam, oleum, aere) extinguendas; Dual medium extinguitur; Martensite graditur extinguantur; Martensite graditur extinxit modum infra MS punctum; Bainite isothermal extinguatur modum; Compositis extinguitur modum; Prechooling isothermal extinguitur modum; Moram refrigerationem extinguitur modum; Quenching auto-temperatio modum; RAMULUS Quenching modum, etc.
I. Una medium (aqua, oleum, aere) extinguitur
Single-medium (aquam, oleum, aere) extinguetur: et workpiece quod est calefacta ad extinxit temperatus extinguitur in extinxit medium ad refrigeret omnino. Hoc est simplicissima extinguere modum et saepe usus est in ipsum ferro et Alloy ferro workpieces cum simplex figuris. Et extinguatur medium est electus secundum calorem translationem coefficientem, hardenability, magnitudine, figura, etc ex parte.
II. Duplici Medium Quenching
Dual-medium quenching: The workpiece heated to the quenching temperature is first cooled to close to the Ms point in a quenching medium with strong cooling capacity, and then transferred to a slow-cooling quenching medium to cool to room temperature to reach different quenching cooling temperature ranges and have Relatively ideal quenching cooling rate. Hoc modo est saepe usus est in partes et complexu figuris vel magna workpieces factum de summus ipsum ferro et Alloy ferro. Steels Saepe usus est Steels Steels. Communiter usus refrigerationem media includit aqua-oleum, aqua, nitrate, aqua, aere, et oleum-aere. Plerumque, aquae usus est ut celeri refrigerationem extinguat medium, et oleum vel aer adhibetur ut tardus refrigerationem extinguantur medium. Aeris est raro usus.
III. Martensite gradus Quenhing
Martensitic graded quenching: the steel is austenitized, and then immersed in a liquid medium (salt bath or alkali bath) with a temperature slightly higher or slightly lower than the upper Martensite point of the steel, and maintained for an appropriate time until the inner and outer surfaces of the steel parts After the layers reach the medium temperature, they are taken out for air cooling, and the supercooled austenite is slowly transformed into Martensite per extinxit processus. Est plerumque usus est ad parvum workpieces cum complexu figuris et stricte deformatio requisita. Hoc modum est etiam communiter pro extinxit summus celeritas ferro et summus ally ferro instrumenta et formam.
IV. Martensite gradus Quenching modus infra MS Point
Martensite graditur extinguantur modum infra MS punctum: cum balneum temperatus est inferior quam MS de workpiece ferro et altior quam MF, workpiece refrigescit citius in balneum, et in magnitudine est maior. Saepe usus est maior ferro workpieces et humilis hardenability.
V. Bainite isothermal Quenching Ratio
Bainite isothermal extinguas modum: et workpiece extinguitur in balneum cum inferiore Bainite temperatus de ferro et isothermal, ut in Bainite Member XXX ad LX minuta. Et Baini Austumompering processus habet tres principalis gradus: ① Austenitizing curatio; ② Post-Austenitizing Refrigerant curatio; ③ Bainite isothermal curatio; Communiter in Alloy Steel, High Carbon Steel parva-magnitudine partes et Ductile ferrum castings.
VI. Compositis restrictius modum
Compositis extinguere modum: primo extinguet in workpiece ut infra MS ad obtain Martensite cum a volumine fraction of X% ad XXX% et isotherm in inferioribus Structures ad maius cross-section. Hoc est communiter solebat alloy tool ferro workpieces.
VII. Praechooling et isothermal extinguitur modum
Pre-refrigerationem isothermal extinxit modum: etiam vocavit calefactio isothermal extinxit, in partes sunt primi refrigeratum in balneum cum inferior temperatus (maius MS) et transire ad lotus est superioris. Est idoneam ad ferro partes pauperes hardenenability vel magna workpieces quod debet austempered.
VIII. Moram refrigerationem et extinguitur modum
Moram refrigerationem extinguendas modum: Partes primi pre-refrigeratum in aere, calida aqua, aut sal balneum ad temperatus leviter altius quam Ar3 aut Ar1 et unum medium extinguitur. Saepe usus est in partes cum complexu figuris et late varias crasnesses in variis partibus et postulantes parva deformatio.
IX. Quenching et auto-tempering modum
Exstinguit et sui temperatio modum: tota workpiece ut processionaliter succensus est, sed in extinguendo, nisi ex parte, quod necessitates ad indurari (plerumque operationem partem) baptizari in extinguitur liquido et cooled. Cum ignis colore de unimmersed parte evanescit statim tollet in aere. Medium refrigerationem extinguantur processus. In extinguendo et auto-temperatio modum utitur calor ex core quod non omnino refrixerit transferre ad superficiem ad ingenium superficiem. Tools communiter ad resistere impulsum ut chisels, pugnis, malleis, etc.
X. Spray Quenching Methodo
RAMULUS Quenching Methodo: A extinguitur modum in quo aqua est sprayed onto workpiece. Aquae fluxus potest esse magna aut parva, secundum quod requiritur extinguitur altitudinem. RAMULUS extinguere modum non formare vapor film super superficiem workpiece, ita cursus altius obcurabatur iacuit quam aqua extinguantur. Maxime propter loci superficiem extinguendo.