Normae Aequivalentes Ferri Resistentis Detritioni/Abrasioni
Gradus Chalybis | SSAB | JFE | DILLIDUR | ThyssenkKrupp | Ruukki |
NM360 | - | EH360 | - | - | - |
NM400 | HARDOX400 | EH400 | 400V | XAR400 | Raex400 |
NM450 | HARDOX450 | - | 450V | XAR450 | Raex450 |
NM500 | HARDOX500 | EH500 | 500V | XAR500 | Raex500 |
Chalybs Resistens Detritioni/Abrasioni --- Norma Sinensis
● NM360
● NM400
● NM450
● NM500
● NR360
● NR400
● B-HARD360
● B-HARD400
● B-HARD450
● KN-55
● KN-60
● KN-63
Compositio Chemica (%) Chalybis NM Resistentis Attritioni
Gradus Chalybis | C | Si | Mn | P | S | Cr | Mo | B | N | H | Ceq |
NM360/NM400 | ≤0.20 | ≤0.40 | ≤1.50 | ≤0.012 | ≤0.005 | ≤0.35 | ≤0.30 | ≤0.002 | ≤0.005 | ≤0.00025 | ≤0.53 |
NM450 | ≤0.22 | ≤0.60 | ≤1.50 | ≤0.012 | ≤0.005 | ≤0.80 | ≤0.30 | ≤0.002 | ≤0.005 | ≤0.00025 | ≤0.62 |
NM500 | ≤0.30 | ≤0.60 | ≤1.00 | ≤0.012 | ≤0.002 | ≤1.00 | ≤0.30 | ≤0.002 | ≤0.005 | ≤0.0002 | ≤0.65 |
NM550 | ≤0.35 | ≤0.40 | ≤1.20 | ≤0.010 | ≤0.002 | ≤1.00 | ≤0.30 | ≤0.002 | ≤0.0045 | ≤0.0002 | ≤0.72 |
Proprietates Mechanicae Chalybis NM Resistentis Attritioni
Gradus Chalybis | Robur Cedendi /MPa | Robur tensile /MPa | Elongatio A50 /% | Hardess (Brinell) HBW10/3000 | Impactus/J (-20℃) |
NM360 | ≥900 | ≥1050 | ≥12 | 320-390 | ≥21 |
NM400 | ≥950 | ≥1200 | ≥12 | 380-430 | ≥21 |
NM450 | ≥1050 | ≥1250 | ≥7 | 420-480 | ≥21 |
NM500 | ≥1100 | ≥1350 | ≥6 | ≥470 | ≥17 |
NM550 | - | - | - | ≥530 | - |
Chalybs Resistens Detritioni/Abrasioni --- Norma Americana
● AR400
● AR450
● AR500
● AR600
Disponibilitas Laminae Chalybis Resistentis Abrasioni
Gradus | Crassitudo | Latitudo | Longitudo |
AR200 / AR235 | 3/16" – 3/4" | 48" – 120" | 96" – 480" |
AR400F | 3/16" – 4" | 48" – 120" | 96" – 480" |
AR450F | 3/16" – 2" | 48" – 96" | 96" – 480" |
AR500 | 3/16" – 2" | 48" – 96" | 96" – 480" |
AR600 | 3/16" – 3/4" | 48" – 96" | 96" – 480" |
Compositio Chemica Laminae Chalybis Abrasioni Resistentis
Gradus | C | Si | Mn | P | S | Cr | Ni | Mo | B |
AR500 | 0.30 | 0.7 | 1.70 | 0.025 | 0.015 | 1.00 | 0.70 | 0.50 | 0.005 |
AR450 | 0.26 | 0.7 | 1.70 | 0.025 | 0.015 | 1.00 | 0.70 | 0.50 | 0.005 |
AR400 | 0.25 | 0.7 | 1.70 | 0.025 | 0.015 | 1.50 | 0.70 | 0.50 | 0.005 |
AR300 | 0.18 | 0.7 | 1.70 | 0.025 | 0.015 | 1.50 | 0.40 | 0.50 | 0.005 |
Proprietates Mechanicae Laminae Chalybis Abrasioni Resistentis
Gradus | Robur Cedendi MPa | Robur tensile MPa | Elongatio A | Robur Impactus Charpy V 20J | Intervallum Duritudinis |
AR500 | 1250 | 1450 | 8 | -30°C | 450-540 |
AR450 | 1200 | 1450 | 8 | -40°C | 420-500 |
AR400 | mille | 1250 | 10 | -40°C | 360-480 |
AR300 | 900 | mille | 11 | -40°C | - |
Applicationes Laminae Ferreae Resistentis Abrasioni
● Laminae AR235 ad usus detritionis moderatae destinantur, ubi resistentiam detritionis meliorem praebent comparatione cum chalybe carbonico structurali.
● AR400 sunt laminae chalybis abrasioni resistentis optimae, quae calore tractatae sunt et perdurationem exhibent. Facultates formationis et nexus emendatae.
● AR450 est lamina abrasioni resistens, in variis applicationibus adhibita ubi paulo maior firmitas quam AR400 desideratur.
● Laminae AR500 ad usus fodinarum, silviculturae et constructionis aptae sunt.
● AR600 in locis magnae detritionis, ut in remotione aggregatorum, fodina, et fabricatione sitularum et corporum detritionis, adhibetur.
Lamina ferrea abrasioni resistente (AR) typice in statu laminato fabricatur. Huiusmodi laminarum ferrearum genera ad longam vitam utilem in condicionibus asperis elaborata sunt. Producta AR apta sunt variis applicationibus in campis ut fodinis/lapidicinis, convectionibus, tractatione et constructione materiarum, et motus terrae. Designatores et operarii officinarum laminam ferream AR eligunt cum vitam utilem partium criticarum extendere et pondus cuiusque unitatis in usum missae reducere student. Commoda usus laminae ferri resistentis attritioni in applicationibus quae impactum et/vel contactum labens cum materia abrasiva implicant immensa sunt.
Laminae chalybis mixtae, quae abrasivas resistunt, plerumque bonam resistentiam contra lapsum et abrasionem impacti offerunt. Magnum carbonis contentum in mixtura duritiem et tenacitatem chalybis auget, ita ut materia idealis sit ad usus qui magnam resistentiam impacti vel abrasioni requirunt. Magna duritia cum chalybe carbonis alto obtineri potest, et chalybs bonam resistentiam penetrationi habebit. Tamen, celeritas detritionis celeris erit comparata cum lamina mixta calore tractata, quia chalybs carbonis alto fragilis est, ita particulae facilius a superficie avelli possunt. Propterea, chalybes carbonis alto ad usus magnae detritionis non adhibentur.
Delineatio singularis


-
Lamina Ferrea Abrasioni Resistentis (AR)
-
Lamina Ferrea AR400 AR450 AR500
-
NM400 NM450 Chalybs Abrasioni Resistens
-
Lamina Ferrea AR400
-
Lamina Ferrea Tempestatis Gradus Corten
-
Laminae Corten S355J2W Laminae Ferreae Extenuantiae
-
Laminae Ferreae Corten ad Temperiem Exercendam ASTM A606-4
-
Lamina Ferrea Extra Litus S355G2
-
Lamina Ferrea Structuralis S355
-
Trabes/Vectis T ex Chalybe Structurali S355JR